AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST 24
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) …………….……..……….………… 12-14
Main Chemical Component
Al2O3 (%) ………………………………………… 42
SiO2 (%) …………………………………………… 37
Fe2O3 (%) …………………………………………. 5
CaO (%) …………………………………………… 10
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1350
Bulk Density at 110 ºC (gr/cm³) …. 2.15-2.25
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 250-350
After Firing at 1300 ºC ……………. 250-350
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.5) to (+0.3)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST 25
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) …………….……..……….………… 11-13
Main Chemical Component
Al2O3 (%) ………………………………………… 45
SiO2 (%) …………………………………………… 40
Fe2O3 (%) ……………………………………….. 1.5
CaO (%) …………………………………………….. 8
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1375
Bulk Density at 110 ºC (gr/cm³) …. 2.15-2.30
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 300-400
After Firing at 1300 ºC ……………. 300-400
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.5) to (+0.3)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST 28
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) …………….……..……….………….. 9-11
Main Chemical Component
Al2O3 (%) ………………………………………… 56
SiO2 (%) ………………………………………… 36.5
Fe2O3 (%) ……………………………………….. 1.3
CaO (%) ………………………………………….. 4.2
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1500
Bulk Density at 110 ºC (gr/cm³) …. 2.25-2.35
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 600-800
After Firing at 1300 ºC ……………. 500-700
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.4) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A50
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) …………….……..……….….…….. 13-15
Main Chemical Component
Al2O3 (%) ………………………………………… 50
SiO2 (%) …………………………………………… 34
Fe2O3 (%) ……………………………………….. 1.7
CaO (%) …………………………………………….. 9
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1395
Bulk Density at 110 ºC (gr/cm³) …. 2.15-2.25
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 300-400
After Firing at 1300 ºC ……………. 350-450
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.5) to (+0.3)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A50S
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) …………….……..……….………….. 9-11
Main Chemical Component
Al2O3 (%) ………………………………………… 52
SiO2 (%) …………………………………………… 37
Fe2O3 (%) ……………………………………….. 1.3
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1500
Bulk Density at 110 ºC (gr/cm³) …. 2.25-2.35
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 600-800
After Firing at 1300 ºC ……………. 500-700
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.4) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A60
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) …………….……..……….….…….. 10-12
Main Chemical Component
Al2O3 (%) ………………………………………… 60
SiO2 (%) …………………………………………… 28
Fe2O3 (%) ……………………………………….. 1.6
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1540
Bulk Density at 110 ºC (gr/cm³) …. 2.25-2.35
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 600-800
After Firing at 1300 ºC ……………. 500-700
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.4) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A70
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) …………….……..……….….…….. 10-12
Main Chemical Component
Al2O3 (%) ………………………………………… 70
SiO2 (%) …………………………………………… 19
Fe2O3 (%) ……………………………………….. 1.5
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1600
Bulk Density at 110 ºC (gr/cm³) …. 2.35-2.45
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 600-800
After Firing at 1300 ºC ……………. 500-700
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.3) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A80
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………………..……….….…….. 8-10
Main Chemical Component
Al2O3 (%) ………………………………………… 80
SiO2 (%) …………………………………………… 11
Fe2O3 (%) …………………………………………. 2
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1640
Bulk Density at 110 ºC (gr/cm³) …. 2.55-2.65
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 650-850
After Firing at 1300 ºC ……………. 600-800
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.3) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A80B
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………………..……….….…….. 8-10
Main Chemical Component
Al2O3 (%) ………………………………………… 78
BaO (%) ………………………………………….. 5.5
SiO2 (%) ………………………………………….. 6.5
Fe2O3 (%) ……………………………………….. 1.7
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1500
Bulk Density at 110 ºC (gr/cm³) …. 2.60-2.80
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 650-850
After Firing at 1300 ºC ……………. 600-800
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.3) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A85
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………………..……….….…….. 8-10
Main Chemical Component
Al2O3 (%) ………………………………………… 85
SiO2 (%) ………………………………………….. 6.5
Fe2O3 (%) …………………………………………. 2
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1680
Bulk Density at 110 ºC (gr/cm³) …. 2.60-2.70
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 700-900
After Firing at 1300 ºC ……………. 700-900
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A85B
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………………..……….….…….. 8-10
Main Chemical Component
Al2O3 (%) ………………………………………… 88
BaO (%) ………………………………………….. 5.5
SiO2 (%) ……………………………………………. 1
Fe2O3 (%) ……………………………………….. 0.5
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1700
Bulk Density at 110 ºC (gr/cm³) …. 2.70-2.90
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 750-950
After Firing at 1300 ºC ……………. 750-950
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A90
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………………..……….….…….. 8-10
Main Chemical Component
Al2O3 (%) ………………………………………… 90
SiO2 (%) ………………………………………….. 3.5
Fe2O3 (%) …………………………………………. 1
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1740
Bulk Density at 110 ºC (gr/cm³) …. 2.65-2.85
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………….. 750-950
After Firing at 1300 ºC ……………. 750-950
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A94
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………….….…..……….….…….. 8-9
Main Chemical Component
Al2O3 (%) ………………………………………… 94
SiO2 (%) ………………………………………….. 1.2
Fe2O3 (%) ……………………………………….. 0.4
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1800
Bulk Density at 110 ºC (gr/cm³) …. 2.75-2.95
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …….….….. 800-1000
After Firing at 1300 ºC …….….…. 800-1000
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A95
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………….….…..……….….…….. 8-9
Main Chemical Component
Al2O3 (%) ………………………………………… 95
SiO2 (%) ………………………………………….. 0.6
Fe2O3 (%) ……………………………………….. 0.3
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1800
Bulk Density at 110 ºC (gr/cm³) …. 2.75-2.95
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …….….….. 800-1000
After Firing at 1300 ºC …….….…. 800-1000
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
AZARSHAHAB REFRACTORIES CO.
Conventional Castables
ARCAST A96
General Properties (Download PDF)
Classification …………….……..…..……….. Alumina Castable
Description…Classical Hydraulic Bonded Refractory Castable
Raw Material Basis …………….……………….……. Chamotte
Bond ………………….….………………….…………. Hydraulic
Installing Method …………………………… Casting / Vibrating
Packaging ……….……….. 25 kg net weight multi proof sacks
Storage Life (Month) …………….…………………..……..….. 9
Grain Size (mm) ………………………………………….. Max 6
Water Required (%) ……………….….…..……….….…….. 7-9
Main Chemical Component
Al2O3 (%) ………………………………………… 96
SiO2 (%) ………………………………………….. 0.1
Fe2O3 (%) ……………………………………….. 0.1
CaO (%) …………………………………………… 3.6
Physical & Thermal Properties
Maximum Service Temperature (ºC) … 1830
Bulk Density at 110 ºC (gr/cm³) …. 2.80-3.00
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …….….….. 800-1000
After Firing at 1300 ºC …….….…. 800-1000
Permanent Linear Change (%)
After Drying at 110 ºC …….……… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.