ARGUN 25V
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN 25V
General Properties (Download PDF)
Classification …………….….….………Insulating Gunning
Description…Light Weight Hydraulic Bonded Refractory Gunning
Raw Material Basis ………..……….…..……… Vermiculite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 4
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 25
SiO2 (%) …………………………………………… 28
Fe2O3 (%) ……………………………………… 14.5
CaO (%) …………………………………………… 20
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1000
Bulk Density at 1000 ºC (gr/cm³) … 0.55-0.70
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………….….. 5-15
After Firing at 1000 ºC ………..………… 5-15
Permanent Linear Change (%)
After Drying at 110 ºC ……..… (-0.5) to (-0.2)
After Firing at 800 ºC ………… (-1.5) to (-0.6)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARGUN 30V
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN 30V
General Properties (Download PDF)
Classification …………….….….………Insulating Gunning
Description…Light Weight Hydraulic Bonded Refractory Gunning
Raw Material Basis ………..……….…..……… Vermiculite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 4
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 30
SiO2 (%) …………………………………………… 32
Fe2O3 (%) ………………………………………….. 8
CaO (%) …………………………………………… 18
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1055
Bulk Density at 1000 ºC (gr/cm³) … 0.55-0.75
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………….….. 5-15
After Firing at 1000 ºC ………..………… 5-15
Permanent Linear Change (%)
After Drying at 110 ºC ……..… (-0.6) to (-0.2)
After Firing at 800 ºC ………… (-2.0) to (-1.5)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARGUN A50
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN A50
General Properties (Download PDF)
Classification ………………..………Alumina Gunning Mix
Description…Classical Hydraulic Bonded Refractory Gunning
Raw Material Basis ………..………………..……… Bauxite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 6
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 50
SiO2 (%) …………………………………………… 33
Fe2O3 (%) ……………………………………….. 1.5
CaO (%) …………………………………………….. 9
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1395
Bulk Density at 1000 ºC (gr/cm³) …… 2.1-2.2
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………… 300-400
After Firing at 1350 ºC ……….…….. 320-420
Permanent Linear Change (%)
After Drying at 110 ºC ………….… Negligible
After Firing at 1000 ºC ……… (-0.5) to (+0.3)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARGUN A60
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN A60
General Properties (Download PDF)
Classification ………………… High Alumina Gunning Mix
Description…Classical Hydraulic Bonded Refractory Gunning
Raw Material Basis ………..………………..……… Bauxite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 6
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 60
SiO2 (%) …………………………………………… 28
Fe2O3 (%) …………………………………………. 2
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1540
Bulk Density at 1000 ºC (gr/cm³) … 2.25-2.35
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………… 400-600
After Firing at 1350 ºC ………..……. 420-620
Permanent Linear Change (%)
After Drying at 110 ºC ………….… Negligible
After Firing at 1000 ºC ………. (-0.4) to (-0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARGUN A70
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN A70
General Properties (Download PDF)
Classification ………………… High Alumina Gunning Mix
Description…Classical Hydraulic Bonded Refractory Gunning
Raw Material Basis ………..………………..……… Bauxite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 6
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 70
SiO2 (%) …………………………………………… 19
Fe2O3 (%) ……………………………………….. 1.5
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1600
Bulk Density at 1000 ºC (gr/cm³) … 2.45-2.55
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………… 420-620
After Firing at 1350 ºC ………..……. 450-650
Permanent Linear Change (%)
After Drying at 110 ºC ………….… Negligible
After Firing at 1000 ºC ………. (-0.3) to (-0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARGUN A80
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN A80
General Properties (Download PDF)
Classification ………………… High Alumina Gunning Mix
Description…Classical Hydraulic Bonded Refractory Gunning
Raw Material Basis ………..………………..……… Bauxite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 6
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 82
SiO2 (%) …………………………………………….. 9
Fe2O3 (%) ………………………………………….. 2
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1640
Bulk Density at 1000 ºC (gr/cm³) … 2.50-2.60
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………… 450-650
After Firing at 1400 ºC ………..……. 500-700
Permanent Linear Change (%)
After Drying at 110 ºC ………….… Negligible
After Firing at 1000 ºC ………. (-0.3) to (-0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARGUN A85
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN A85
General Properties (Download PDF)
Classification ………………… High Alumina Gunning Mix
Description…Classical Hydraulic Bonded Refractory Gunning
Raw Material Basis ………….… Tabular Alumina /Bauxite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 6
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 85
SiO2 (%) …………………………………………….. 7
Fe2O3 (%) ………………………………………….. 2
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1680
Bulk Density at 1000 ºC (gr/cm³) … 2.60-2.70
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………… 500-700
After Firing at 1400 ºC ………..……. 550-750
Permanent Linear Change (%)
After Drying at 110 ºC ………….… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARGUN A94
AZARSHAHAB REFRACTORIES CO.
GUNNING MIX
ARGUN A94
General Properties (Download PDF)
Classification ………………… High Alumina Gunning Mix
Description…Classical Hydraulic Bonded Refractory Gunning
Raw Material Basis ………….… Tabular Alumina /Bauxite
Bond ………………….………………….………… Hydraulic
Installing Method …………………………………. Gunning
Packaging ……………..20 kg net weight multi proof sacks
Storage Life (Month) …..…..……………..…..…………… 9
Grain Size (mm) ……….……….….….……………… Max 6
Water Required (%) …….…..……….….….. Nozzle Added
Main Chemical Component
Al2O3 (%) ………………………………………… 93
SiO2 (%) ………………………………………….. 2.7
Fe2O3 (%) ……………………………………….. 0.1
CaO (%) …………………………………………….. 4
Physical & Thermal Properties
Maximum Service Temperature (ºC) .… 1800
Bulk Density at 1000 ºC (gr/cm³) … 2.80-2.90
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC ……………… 600-800
After Firing at 1400 ºC ………..……. 650-850
Permanent Linear Change (%)
After Drying at 110 ºC ………….… Negligible
After Firing at 1000 ºC ……… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.