AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A45SiC10LCC
General Properties (Download PDF)
Classification………………………..….……… Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ……………………. Low Iron Chamotte/SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 45
SiO2 (%) …………………………………………. 38
Fe2O3 (%) ……………………………………… 1.5
CaO (%) …………………………………………. 2.5
SiC (%) …………………………………………… 10
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1500
Bulk Density at 110 ºC (gr/cm³) ……… 2.35-2.55
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 700-900
After Firing at 1400 ºC …………….…… 800-1000
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.3) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A40SiC20LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A40SiC20LCC
General Properties (Download PDF)
Classification………………………..….……… Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ……………………. Low Iron Chamotte/SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 40
SiO2 (%) …………………………………………. 33
Fe2O3 (%) ……………………………………… 1.5
CaO (%) …………………………………………. 2.5
SiC (%) …………………………………………… 20
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1490
Bulk Density at 110 ºC (gr/cm³) ……… 2.35-2.55
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 700-900
After Firing at 1400 ºC …………….…… 800-1000
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.3) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A35SiC30LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A35SiC30LCC
General Properties (Download PDF)
Classification………………………..….……… Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ……………………. Low Iron Chamotte/SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 35
SiO2 (%) …………………………………………. 29
Fe2O3 (%) ……………………………………… 1.5
CaO (%) …………………………………………. 2.5
SiC (%) …………………………………………… 30
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1470
Bulk Density at 110 ºC (gr/cm³) ……… 2.35-2.55
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 700-900
After Firing at 1400 ºC …………….…… 800-1000
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.3) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST 30ADSiC60 LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST 30ADSiC60 LCC
General Properties (Download PDF)
Classification………………………..….……… Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ..…………………………… Andalusite / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 5.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 25
SiO2 (%) …………………………………………. 12
Fe2O3 (%) ……………………………………… 0.5
CaO (%) ……………………………………………. 2
SiC (%) …………………………………………… 60
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1600
Bulk Density at 110 ºC (gr/cm³) ……… 2.55-2.75
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 700-900
After Firing at 1400 ºC …………….…….. 750-950
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST 40ADSiC30 LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST 40ADSiC30 LCC
General Properties (Download PDF)
Classification………………………..….……… Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ..…………………………… Andalusite / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 5.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 42
SiO2 (%) …………………………………………. 24
Fe2O3 (%) ……………………………………… 0.6
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 30
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1600
Bulk Density at 110 ºC (gr/cm³) ……… 2.55-2.75
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….….. 800-1000
After Firing at 1400 ºC …………….…….. 700-900
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST 55ADSiC10LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST 55ADSiC10LCC
General Properties (Download PDF)
Classification………………………..….……… Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ..…………………………… Andalusite / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 5.5-7.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 55
SiO2 (%) …………………………………………. 31
Fe2O3 (%) ……………………………………… 0.8
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 10
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1620
Bulk Density at 110 ºC (gr/cm³) ……… 2.55-2.75
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 600-800
After Firing at 1400 ºC …………….…….. 700-900
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.2) to (+0.2)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A70SiC10LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A70SiC10LCC
General Properties (Download PDF)
Classification………………………..…… High Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ………………………………… Bauxite / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 73
SiO2 (%) ………………………………………… 9.5
Fe2O3 (%) ……………………………………… 1.8
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 10
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1700
Bulk Density at 110 ºC (gr/cm³) ……… 2.68-2.88
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 700-900
After Firing at 1400 ºC …………….…… 900-1100
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.3) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A65SiC20LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A65SiC20LCC
General Properties (Download PDF)
Classification………………………..…… High Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ………………………………… Bauxite / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 65
SiO2 (%) ………………………………………… 8.5
Fe2O3 (%) ……………………………………… 1.5
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 20
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1680
Bulk Density at 110 ºC (gr/cm³) ……… 2.68-2.88
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 700-900
After Firing at 1400 ºC …………….…… 850-1050
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.3) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A55SiC30LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A55SiC30LCC
General Properties (Download PDF)
Classification………………………..…… High Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ………………………………… Bauxite / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.5-6.5
Main Chemical Component
Al2O3 (%) ……………………………………….. 56
SiO2 (%) …………………………………………… 8
Fe2O3 (%) ……………………………………… 1.4
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 30
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1660
Bulk Density at 110 ºC (gr/cm³) ……… 2.68-2.88
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….……. 700-900
After Firing at 1400 ºC …………….…… 800-1000
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.3) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A80SiC10LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A80SiC10LCC
General Properties (Download PDF)
Classification………………………..…… High Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ………………………. Tabular Alumina / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.0-6.0
Main Chemical Component
Al2O3 (%) ……………………………………….. 80
SiO2 (%) …………………………………………. 6.5
Fe2O3 (%) ……………………………………… 0.5
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 10
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1840
Bulk Density at 110 ºC (gr/cm³) ……… 2.85-3.05
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….….. 900-1100
After Firing at 1400 ºC …………….…. 1000-1200
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.2) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A70SiC20LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A70SiC20LCC
General Properties (Download PDF)
Classification………………………..…… High Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ………………………. Tabular Alumina / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.0-6.0
Main Chemical Component
Al2O3 (%) ……………………………………….. 70
SiO2 (%) …………………………………………. 6.5
Fe2O3 (%) ……………………………………… 0.5
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 20
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1830
Bulk Density at 110 ºC (gr/cm³) ……… 2.85-3.05
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….….. 900-1100
After Firing at 1400 ºC …………….…. 1000-1200
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.2) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.
ARCAST A60SiC30LCC
AZARSHAHAB REFRACTORIES CO.
LCC & SILICON CARBIDE
ARCAST A60SiC30LCC
General Properties (Download PDF)
Classification………………………..…… High Alumina Castable
Description … Low Cement Hydraulic Bonded Refractory Castable
Raw Material Basis ………………………. Tabular Alumina / SiC
Bond ……………….………………………….…………. Hydraulic
Installing Method …………………………….. Casting / Vibrating
Packaging …………….……. 25 kg net weight multi proof sacks
Storage Life (Month) …………………………………..…..….… 9
Grain Size (mm) …………………………….….….………. Max 6
Water Required (%) ……….…………………….……….. 4.0-6.0
Main Chemical Component
Al2O3 (%) ……………………………………….. 60
SiO2 (%) …………………………………………… 7
Fe2O3 (%) ……………………………………… 0.5
CaO (%) ………………………………………….. 2.5
SiC (%) ……………………………………………. 30
Physical & Thermal Properties
Maximum Service Temperature (ºC) …..…. 1820
Bulk Density at 110 ºC (gr/cm³) ……… 2.85-3.05
Cold Crushing Strength (kg/cm²)
After Drying at 110 ºC …………..….….. 900-1100
After Firing at 1400 ºC …………….…. 1000-1200
Permanent Linear Change (%)
After Drying at 110 ºC ……………..……Negligible
After Firing at 1000 ºC …………… (-0.2) to (+0.1)
All data subject to reasonable deviation and therefore, should not be used for specification purposes.